Item: PP (Polypropylene)
Type: Virgin
Grade: Homopolymer&Copolymer&Random Copolymer
Packing: 25kg in pp bag
Color: Natural
Specifications,
1, PP Homopolymer
Tests |
Value |
Unit |
Melt Flow Rate |
16±3 |
g/10min |
Cleanness |
5 |
/kg≤ |
Tensile Yield Stress |
33 |
Mpa≥ |
isotacticity |
94 |
%≥ |
Unnotched Izod impact strength(23°C) |
29 |
j/m≥ |
Powder ash |
0.02 |
%≤ |
Heat Deflection Temperature |
85 |
°C≥ |
Packing |
25kg in PP bag,20MT/1X20'FCL |
2, PP Copolymer
Tests |
Value |
Unit |
Melt Flow Rate |
45 |
g/10min |
Density |
0.90 |
G/cm3 |
Elongation Stress |
10 |
% |
Flexural modulus |
14 |
Mpa |
Rockwell hardness |
95 |
R scale |
IZOD impact strength |
6.5 |
kg.cm/cm |
Vicat softening point |
152 |
°C |
Heat distortion temperature |
125 |
°C |
Packing |
25kg in pp bag,20mt/1x20'FCL |
3, PP Random Copolymer (PPR)
Tests |
Value |
Unit |
Method |
Melt Flow Rate (MFR) |
0.45 |
g/10min |
GB 3682 |
Density |
0.91 |
g/cm3 |
ASTM D-1505 |
Tensile Strength at Yield |
24 |
Mpa |
GB 1040 |
Elongation at Break |
750 |
% |
GB 1040 |
Rockwellhardness |
85 |
J/M |
GB 9342 |
Izod impact strength |
65 |
J/M |
ASTM D-256 |
Packing |
25kg in pp bag,20MT/1X20'FCL |
Application,
Fiber (Carpet, Textiles, Upholstery, etc.)
Film (Shopping bags, casting film, multilayer film, etc.)
Blow Molding (Medical & Cosmetic container, Lubricant & Paint container, etc)
Extrusion Molding (Sheet, Pipe, Wire & Cable, etc.)
Injection Molding (Automotive, Electronic, Construction, House wares, Furniture, Toys, etc.)